Polysiloxane-modified hybrid Nafion membranes were prepared by casting a mixture of Nafion solution and a precursor of acid functionalised polysiloxane based on tetraethoxysilane and a mercaptan-organoalkoxysilane. Scanning Electron Microscopy (SEM) and Atomic Force Microscopy analysis revealed that the functionalised polysiloxane was dispersed either as finely nanosized inclusions or as coarse domains depending on the rate of the solvent evaporation during the casting procedure. In particular the slower is the rate of solvent evaporation the more interpenetrated and homogenously dispersed at nanosized level is the polysiloxane inside the Nafion membrane. The hybridization process increases the thermal stability of the membranes of about 50 degrees C relatively to the unmodified Nafion. Small angle X-ray scattering (SAXS) analysis reveals that the hybrid membranes exhibited the typical morphology of Nafion consisting of distinct hydrophilic and hydrophobic domains. Water vapor sorption and proton conductivity were measured varying the temperature (up to 120 degrees C) and the water activity conditions (from 0.1 to 0.8). The polysiloxane network always increases the water vapor uptake of the membranes and increases significantly the proton conductivity at higher temperature depending on the type of morphology developed by the manufacturing method. in particular hybrid membranes exhibiting nanosized polysiloxane dispersion show a proton conductivity which is up to one-and-half time higher than Nafion recast membrane at high temperature and low water content. (C) 2009 Elsevier B.V. All rights reserved.