Textile fibers and yarns of high conductivity, and their integration into wearable textiles for different electronic applications, have become an important research field for many research groups throughout the world. We have produced novel electrically conductive textile yarns by vapor-phase polymerization (VPP) of a conjugated polymer, poly(3,4-ethylenedioxythiophene) (PEDOT), on the surface of commercially available textile yarns (viscose). In this article, we have presented a novel setup for electrical resistance measurements, which can be used not only for fibrous structures but also for woven structures of specific dimensions. We have reported a two-point resistance-measuring method using an already manufactured setup and also a comparison with the conventionally used method (so-called crocodile clip method). We found that the electrical properties of PEDOT-coated viscose fibers strongly depend on the concentration of oxidant (FeCl3) and the doping (oxidation) process of PEDOT. To evaluate the results, we used mass specific resistance values of PEDOT-coated viscose yarns instead of normal surface resistance values. The voltagecurrent (VI) characteristics support the ohmic behavior of coated fibers to some extent. Monitoring of the charging effect of the flow of current through conductive fibers for prolonged periods of time showed that conductivity remains constant. The change in electrical resistance values with increase in the length of coated fibers was also reported. The resistance-measuring setup employed could also be used for continuous measurement of resistance in the production of conductive fibers, as well as for four-point resistance measurement. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012