Poly(2-acrylamido-2-methylpropanesulfonic acid) (PAMPS) was grafted on the surface of carbon microspheres (CMSs), which were modified in prior by a mixed acid (HNO3 and H2SO4) oxidation and 3-methacryloxypropyl trimethoxysilane silanization. Then, the molecularly imprinting polymerization was carried out towards the macromolecule PAMPS grafted on the surface of CMSs using dibenzothiophene (DBT) as template, ethylene dimethacrylate as cross-linking agent and (NH4)(2)S2O8 (APS) as initiator to prepare surface molecularly imprinted polymer (MIP-PAMPS/CMSs) for adsorbing DBT. The optimized conditions of grafting PAMPS, including AMPS dosage, APS content, reaction temperature and reaction time, were emphasized in this paper. The morphology of the samples was characterized by field emission scanning electron microscopy. The functional groups were analyzed qualitatively by Fourier transform infrared spectrometry. The grafting degree of PAMPS was investigated by thermogravimetry. The results show that the preferable AMPS dosage, APS content, reaction temperature and time were 5 g, 0.15 g, 70 degrees C and 12 h, respectively, for preparing PAMPS/CMSs composite on the basis of 1.0 g of silanized-CMSs. The absorbing characteristic of MIP-PAMPS/CMSs toward DBT was studied preliminarily with dynamic adsorption. In the experiment of dynamic adsorption, MIP-PAMPS/CMSs and non-imprinted polymer (NIP-PAMPS/CMSs) were compared with respect to their rapid adsorption in 1 mmol/L of DBT solution in n-hexane. When the first 1 mL of 1 mmol/L DBT solution was injected and flowed through a column packed with 0.1 g of MIP-PAMPS/CMSs, the content of DBT reduced to 0.265 mmol/L, that is, decreased significantly from 279 to 74 ppm. When 3 mL of DBT solution was flowed through the packed column, the adsorption of MIP-PAMPS/CMSs toward DBT reached saturation with the maximum adsorption amount of 1.38 x 10(-2) mmol/g and the overall adsorption efficiency of 46%, while NIP-PAMPS/CMSs adsorbed only 1.66 x 10(-3) mmol/g of DBT. It is suggested that the MIP-PAMPS/CMSs had much better adsorption property towards DBT than NIP-PAMPS/CMSs. (C) 2012 Elsevier B.V. All rights reserved.