Polyisoprenes (PI) and polybutadienes (PB) both having vinyl-type side chains preferentially were prepared and characterized. Both polymers were anionically polymerized with cumyl potassium or pottassium naphthalenide as initiators in a polar solvent, tetrahydrofuran, at low temperature. From the H-1 NMR measurement, the PI contains 3,4- and 1,2-microstructures and PB does 1,2-microstructure preferentially. All the samples covering the molecular weight range of 37 k <= M-w <= 724 k for PI and 35 k <= M-w <= 197 k for PB were confirmed to have narrow molecular weight distribution. Measured glass transition temperatures, i.e., 11.0 degrees C for PI and -0.7 degrees C for PB are both considerably high compared with those of 1,4-microstructure-rich analogues. Intrinsic viscosity measurements in 1,3-dioxane for PI and 2-octanol for PB were carried out, and the segment lengths of the 3,4-/1,2-rich PI and 1,2-rich PB were estimated to be 0.60 nm and 0.59 nm, which are both considerably shorter than the values for two polydienes having 1,4-microstructures preferentially, i.e., 0.66 nm for both 1,4-rich PI and PB. Furthermore plateau moduli of both polymers are determined by dynamic viscoelastic measurements. (c) 2012 Elsevier Ltd. All rights reserved.