The aim of this study was to improve mechanical properties of polypropylene/cycloolefin copolymer (PP/COC) blends by processing-induced formation of long COC fibers. According to the available literature, the fibrous morphology in PP/COC blends was observed just once by coincidence. For this reason, we focused our attention on finding processing conditions yielding PP/COC fibrous morphology in a well-defined, reproducible way. A number of PP/COC blends were prepared by both compression molding and injection molding (IM). Neat polymers were characterized by rheological measurements, whereas phase morphology of the resulting PP/COC blends was characterized by means of scanning electron microscopy (SEM). The longest COC fibers were achieved in the injection molded PP/COC blends with compositions 75/25 and 70/30 wt %. Elastic modulus and yield strength of all blends were measured as functions of the blend composition using an Instron tensile tester; statistically significant improvement of the yield strength due to fibrous morphology was proved. Moreover, two different models were applied in the analysis of mechanical properties: (i) the equivalent box model for isotropic blends and (ii) the Halpin-Tsai model for long fiber composites. In all PP/COC blends prepared by IM, the COC fibers were oriented in the processing direction, as documented by SEM micrographs, and acted as a reinforcing component, as evidenced by stress-strain measurements. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 122: 1168-1175, 2011