Fluoride-Conversion Synthesis of Homogeneous Actinide Oxide Solid Solutions
The synthesis of (U,Th)O-2 solid solutions at a relatively low temperature of 1100 degrees C using a new technique is described. First, separate actinide oxides were reacted with ammonium hydrogen fluoride to form ammonium actinide fluorides at room temperature. Subsequently, this fluoride was converted to an actinide oxide solid solution using a two-phase reaction process, which involved heating of the fluoride first at 610 degrees C in static air followed by heating at 1100 degrees C in flowing argon. Oxide solid solutions of UO2 and ThO2 were synthesized for a ThO2 content from 10 to 90 wt %. Microscopic investigation showed that the (U,Th)O-2 solid solutions synthesized using this method had high crystallinity and homogeneity up to nanoscale.