The optimum Pt and Ru atomic composition of a carbon-supported Pt-Ru alloy (Pt-Ru/C) used in a practical direct methanol fuel cell (DMFC) anode was investigated. The samples were prepared by the polygonal barrel-sputtering method. Based on the physical properties of the prepared Pt-Ru/C samples, the Pt-Ru alloy was found to be deposited on a carbon support. The microscopic characterization showed that the deposited alloy forms nanoparticles, of which the atomic ratios of Pt and Ru (Pt:Ru ratios) are uniform and are in accordance with the overall Pt:Ru ratios of the samples. The formation of the Pt-Ru alloy is also supported by the electrochemical characterization. Based on these results, methanol oxidation on the Pt-Ru/C samples was measured by cyclic voltammetry and chronoamperometry. The results indicated that the methanol oxidation activities of the prepared samples depended on the Pt:Ru ratios, of which the optimum Pt:Ru ratio is 58:42 at.% at 25 degrees C and 50:50 at.% at 40 and 60 degrees C. This temperature dependence of the optimum Pt:Ru ratio is well explained by the relationship between the methanol oxidation reaction process and the temperature, which is reflected in the rate-determining steps considered from the activation energies. It should be noted that at 25-60 degrees C, the Pt-Ru/C with Pt:Ru = 50:50 at.% prepared by our sputtering method has the higher methanol oxidation activity than that of a commercially available sample with the identical overall Pt:Ru ratio. Consequently, the polygonal barrel-sputtering method is useful to prepare the practical DMFC anode catalysts with the high methanol oxidation activity. (C) 2011 Elsevier Ltd. All rights reserved.