Depassivation-repassivation of iron surfaces in boric-borate solutions were investigated by using the micro-indentation test. A pair of current peaks due to repair of the passive film following rupture of the film were observed during a series of indenter drives, i.e., loading and unloading of the indenter. The shape of the current peak depended on environmental conditions (conductivity and pH of the solution) and substrate conditions (mechanical processing history, alloyed element) as well as indentation conditions (repetition, maximum depth, and maximum load). Plastic deformation of the surface was accompanied by surface depassivation, while no depassivation occurred during the elastic deformation, indicating that the passive film on iron has a ductile property. The solution conditions did not affect the scale of depassivation but affected the rate of repassivation. Dislocations in the substrate made surface depassivation difficult but enhanced reactivity during the repassivation. The test also revealed that type-312L stainless steel has high corrosion resistance in a concentrated NaCl solution. (C) 2010 Elsevier Ltd. All rights reserved.