Poly(2'-deoxyadenosine) and poly(thymidine) constructed of carbonate linkages were synthesized by poly-condensation between silyl ether and carbonylimidazolide at the 3'- and 5'-positions of the 2'-deoxyribonucleoside monomers. The N-benzoyl-2'-deoxyadenosine monomer afforded the corresponding polycarbonate together with the cyclic oligomers. However, the deprotection of the N-benzoyl group resulted in the scission of the polymer main chain. Thus, the N-unprotected 2'-deoxyadenosine monomers were examined for polycondensation. However, there was involved the undesired reaction between the adenine amino group and the carbonylimidazolide to form the carbamate linkage. In order to exclude this unfavorable reaction, dynamic protection was employed. Strong hydrogen bonding was used in place of the usual covalent bonding for reducing the nucleophilicity of the adenine amino group. Herein, 3',5'-O-diacylthymidines that form the complementary hydrogen bonding with the adenine amino group were added to the polymerization system of the N-unprotected 2'-deoxyadenosine monomer. Consequently, although the oligomers (M-n = 1000-1500) were produced, the contents of the carbamate group were greatly reduced. The dynamic protection reagents were easily and quantitatively recovered as the MeOH soluble parts from the polymerization mixtures. In the polycondensation of the thymidine monomer, there tended to be involved another unfavorable reaction of carbonate exchange, which consequently formed the irregular carbonate linkages at not only the but also the 3'-3' and positions. Employing the well-designed monomer suppressed the carbonate exchange reaction to produce poly(thymidine) with the almost regular 3'-5'carbonate linkages.