Present work deals with structural, micro-structural and electrical properties of dysprosia stabilized zirconia electrolyte, which have been evaluated by means of X-ray diffraction (XRD) and scanning (SEM), and complex impedance analysis respectively. The amount of dysprosia was varied from 2 to 12 mol% in zirconia. The addition of dysprosia (8-12 mol%) stabilized the cubic zirconia phase, which was analyzed from XRD analysis. SEM micrographs clearly showed the improvement in sinterability with increase in dysprosia concentration up to 6 mol% disprosia. Complex impedance analysis was performed in the temperature range from 250 to 600 degrees C. The results indicated a gradual decrease in impedance of both bulk and grain boundary and increase in conductivity with dysprosia doping up to 6 mol% and thereafter showing a reverse trend. The activation energies for oxygen ion migration were also found to decrease with increase in dysprosia doping which was in the range of 0.99 - 1.28 eV. The average thermal expansion coefficient increases linearly. (C) 2010 Elsevier B.V. All rights reserved.