Sample of nominal composition La0.6Ca0.4Fe0.8Ni0.2O3 (LCFN) was prepared by liquid mix method. The structure of the polycrystalline powder was analyzed with X-ray powder diffraction data. This compound shows orthorhombic perovskite structure with a space group Pnma. In order to improve the electrochemical performance, Sm-doped ceria (SDC) powder was added to prepare the LCFN-SDC composite cathodes. Electrochemical characteristics of the composites have been investigated for possible application as cathode material for an intermediate-temperature-operating solid oxide fuel cell (IT-SOFC). The polarization resistance was studied using Sm-doped ceria (SDC). Electrochemical impedance spectroscopy measurements of LCFN-SDC/SDC/LCFN-SDC test cell were carried out. These electrochemical experiments were performed at equilibrium from 850 degrees C to room temperature, under both zero dc current intensity and air. The best value of area-specific resistance (ASR) was for LCFN cathode doped with 10% of SDC (LCFN-SDC9010), 0.13 Omega cm(2) at 850 degrees C. The dc four-probe measurement exhibits a total electrical conductivity over 100 S cm(-1) at T >= 600 degrees C for LCFN-SDC9010 composite cathode. (C) 2010 Elsevier B.V. All rights reserved.