ABA-type amphiphilic tri-block copolymers were successfully synthesized from poly(ethylene oxide) derivatives through anionic polymerization. When poly(styrene) anions were reacted with telechelic bromine-terminated poly(ethylene oxide) (1) in 2:1 mole ratio, poly(styrene)-b-poly(ethylene oxide)-b-poly(styrene) tri-block copolymers were formed. Similarly, stable telechelic carbanion-terminated poly(ethylene oxide), prepared from 1,1-diphenylethylene-terminated poly (ethylene oxide) (2) and sec-BuLi, was also used to polymerize styrene and methyl methacrylate separately, as a result, poly (styrene)-b-poly(ethylene oxide)-b-poly(styrene) and poly (methyl methacrylate)-b-poly(ethylene oxide)-b-poly(methyl methacrylate) tri-block copolymers were formed respectively. All these tri-block copolymers and poly(ethylene oxide) derivatives, 1 and 2, were characterized by spectroscopic, calorimetric, and chromatographic techniques. Theoretical molecular weights of the tri-block copolymers were found to be similar to the experimental molecular weights, and narrow polydispersity index was observed for all the tri-block copolymers. Differential scanning calorimetric studies confirmed the presence of glass transition temperatures of poly(ethylene oxide), poly(styrene), and poly(methyl methacrylate) blocks in the tri-block copolymers. Poly(styrene)-b-poly(ethylene oxide)-b-poly(styrene) triblock copolymers, prepared from polystyryl anion and 1, were successfully used to prepare micelles, and according to the transmission electron microscopy and dynamic light scattering results, the micelles were spherical in shape with mean average diameter of 106 +/- 5 nm. (C) 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 49: 1376-1386, 2011