The Mobil Composition of Matter No. 41 (MCM-41) containing Cu and Al with Si/Al ratios varying from 100 to 10 and 1 to 6 wt.% of Cu was synthesized under hydrothermal and impregnation conditions, respectively. The samples were characterized by nitrogen adsorption-desorption measurements, X-ray powder diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), UV-Vis diffuse reflectance spectroscopy (UV-Vis DRS), temperature-programmed reduction (TPR), temperature-programmed desorption (TPD), and Si-29 and Al-27 magic-angle spinning-nuclear magnetic resonance (MAS-NMR) spectra. X-ray diffraction patterns indicate that the modified materials retain the standard MCM-41 Structure. TPR patterns show the two-step reduction of Cu species. TPD Study shows that Cu-impregnated Al-MCM-41 samples are more acidic than Al-MCM-41. From the MAS-NMR it was confirmed that most of the Al atoms are present tetrahedrally within the framework and some are present octahedrally in extraframework position. Impregnation of Cu shifted Al to the extraframework position. The catalytic activity of the samples toward hydroxylation of phenol in aqueous medium was evaluated using H2O2 as the oxidant at 80 degrees C. The effects of reaction parameters such as temperature, catalyst amount, amount of H2O2, and solvent were also investigated. Sample containing 4 wt.% copper-loaded Al-MCM-41-100 showed high phenol conversion (78%) with 68% catechol and 32% hydroquinone selectivity. (C) 2009 Elsevier Inc. All rights reserved.