We report the synthesis of poly[(3-hexylthiophene)-block-(3-(4,4,5,5,6,6,7,7,7-nonafluoroheptyl)thi ophene)], P(3HT-b-3SFT), carried out by the Grignard Metathesis Method (GRIM). The copolymers composition was determined by H-1 and F-19 NMR spectroscopies, and gel permeation chromatography (GPC). The thin films of P(3HT-b-3SFT) were investigated by ultraviolet-visible absorption spectroscopy and atomic force microscopy (AFM). We also fabricated bulk-hetero junction (BHJ) solar cells based on blends of P(3HT-b-3SFT) and [6,6]-phenyl-C-61-butyric acid methyl ester (PCBM). Although the composition ratio of P3SFT in P(3HT-b-3SFT) was low, the influence of P3SFT on the morphology and properties of solar cells was significant. The annealing process for the BHJ solar cells induced the formation of large domains and led to poor solar cell performance. The BHJ solar cells, based on PCBM and P(3HT-b-3SFT), prepared by the non-annealing process, had a maximum power conversion efficiency of 0.84% under 100 mW/cm(2) (AM 1.5 solar illumination) in air.