A double-layer coating was prepared on AZ91D alloy by plasma electrolytic oxidation (PEO) plus electroless plating (EP). The plasma eletrolytic oxidation film was prepared in a silicate bath as an inner layer of the coating. Electroless plated Ni-P layer grew from the pores of the PEO film in a nickelous acetate bath and formed as the outer layer of the coating. The microstructure and crystallographic structure was observed with FESEM and XRD. The corrosion resistance of the double-layer coating was evaluated by means of chronopotentiometric (E-t), potentiodynamic polarization (E-i), neutral salt spray test and electrochemical impedance spectroscopy (EIS) test. Compared with the data of as-cast AZ91D magnesium, the open circuit potential of the double-layer coated AZ91D alloy increased by 1.1815 V. while the self-corrosion current density decreased by two orders of magnitude. E-i, EIS result showed that the corrosion resistance of magnesium alloy AZ91D was improved by the double-layer coating. The salt spray test and polarization test results show that the pitting corrosion resistance of AZ91D alloy was improved greatly. An equivalent circuit was proposed to fit the impedance diagrams of AZ91D alloy with the coating. (C) 2010 Elsevier Ltd. All rights reserved.