Journal of Industrial and Engineering Chemistry, Vol.16, No.5, 703-707, September, 2010
DOI10.1016/j.jiec.2010.07.015  Export Citation
The influence of Si-modified TiO2 on the activity of Ag/TiO2 in CO oxidation
Nattaya Comsup, Joongjai Panpranot, and Piyasan Praserthdam†
  • Center of Excellence on Catalysis and Catalytic Reaction Engineering, Department of Chemical Engineering, Faculty of Engineering, Chulalongkorn University, Bangkok 10330, Thailand
E-mail:
Nanocrystalline TiO2 and Si-modified TiO2 with Si/Ti ratios 0.01, 0.05, 0.1, and 0.3 were prepared by the solvothermal method and employed as the supports for Ag/TiO2 catalysts for CO oxidation reaction. The incorporation of Si into the TiO2 lattice in the form of Ti-O-Si as revealed by FT-IR results could inhibit the agglomeration of TiO2 crystallites, resulting in an increase of both surface area andmetal dispersion. However, there existed an optimum content of Si/Ti at ca. 0.05-0.1 which resulted in an improved catalytic activity of Ag/TiO2 in CO oxidation. Based on the O2-temperature programdesorption (O2-TPD) results, the catalysts with appropriate amounts of Si/Ti exhibited higher amount of O2 adsorption and much lower desorption temperature. It is suggested that the presence of Ti-O-Si promoted the formation of active oxygen species and increased the mobility of lattice oxygen so that the catalytic activity was enhanced. There was no improvement in CO oxidation activity of the Ag/TiO2 catalyst when the Si/Ti was further increased to 0.3 due probably to the formation of amorphous SiO2 instead of the Ti-O-Si bond.
Keywords:Si-modified TiO2;CO oxidation;Ag/TiO2
  1. Kongwudthiti S, Praserthdam P, Tanakulrungsank W, Inoue M, J. Mater. Process. Technol., 136, 186 (2003)
  2. del Monte F, Larsen W, Mackenzie JD, J. Am. Ceram. Soc., 83(6), 1506 (2000)
  3. Wiwattanapongpan J, Mekasuwandumrong O, Chaisuk C, Praserthdam P, Ceram. Int., 33, 1469 (2007)
  4. Soisuwan P, Praserthdam P, Panpranot J, Trimm DL, Catal. Commun., 7, 761 (2006)
  5. Fan G, Zou B, Cheng S, Zheng L, J. Ind. Eng. Chem., 16(2), 220 (2010)
  6. Cho K, Chang HK, Park JH, Kim BG, Jang HD, J. Ind. Eng. Chem., 14(6), 860 (2008)
  7. Loong CK, Richardson JW Jr., Ozawa M, Kimura M, J. Alloy Compd., 207, 174 (1994)
  8. Yu J, Wu G, Mao D, Lu G, Acta Phys.-Chim. Sin., 24, 1751 (2008)
  9. Yasuda K, Arai S, Itoh M, Wada K, J. Mater. Sci., 34(15), 3597 (1999)
  10. Ballard J, Davenport J, Lewis C, Doremus R, Schadler L, Nelson W, J. Therm.Spray Technol., 12, 34 (2003)
  11. Alvarez MR, Torralvo MJ, Colloids Surf. A., 113, 165 (1996)
  12. Chang SM, Hou CY, Lo PH, Chang CT, Appl. Catal. B: Environ., 90(1-2), 233 (2009)
  13. Lukac J, Klementova M, Bezdicka P, Bakardjieva S, Subrt J, Szatmary L, Bastl Z, Jirkovsky J, Appl. Catal. B: Environ., 74(1-2), 83 (2007)
  14. Narayanan BN, Yaakob Z, Koodathil R, Chandralayam S, Sugunan S, Saidu FK, Malayattil V, Eur. J. Sci. Res., 28, 566 (2009)
  15. Tauster SJ, Fung SC, Garten RL, J. Am. Chem. Soc., 100, 170 (1978)
  16. Haller GL, Resasco DE, Eley HPDD, Paul BW, Adv. Catal., 36, 173 (1989)
  17. Vannice MA, Sen B, J. Catal., 115, 65 (1989)
  18. Claus P, Schimpf S, Schodel R, Kraak P, Morke W, Honicke D, Appl. Catal. A: Gen., 165(1-2), 429 (1997)
  19. Murrell LL, Yates DJC, Seiyama T, Tanabe K, Stud. Surf. Sci. Catal., 7, 1470 (1981)
  20. Tai Y, Murakami J, Tajiri K, Ohashi F, Date M, Tsubota S, Appl. Catal. A: Gen., 268(1-2), 183 (2004)
  21. Payakgul W, Mekasuwandumrong O, Pavarajarn V, Praserthdam P, Ceram. Int., 31, 391 (2005)
  22. Comsup N, Panpranot J, Praserthdam P, Catal. Lett., 133(1-2), 76 (2009)
  23. Djerdj I, Tonejc AM, J. Alloy Compd., 413, 159 (2006)
  24. Gao BF, Lim TM, Subagio DP, Lim TT, Appl. Catal. A: Gen., 375(1), 107 (2010)
  25. Yang H, Shi R, Zhang K, Hu Y, Tang A, Li X, J. Alloy Compd., 398, 200 (2005)
  26. Jung KY, Park SB, Matsuoka M, Anpo M, Int. J. Photoenergy., 5, 31 (2003)
  27. Yang K, Dai Y, Huang B, Chem. Phys. Lett., 456(1-3), 71 (2008)
  28. Jin RB, Wu ZB, Liu Y, Jiang BQ, Wang HQ, J. Hazard. Mater., 161(1), 42 (2009)
  29. Xu G, Zheng Z, Wu Y, Feng N, Ceram. Int., 35, 1 (2009)
  30. Kang C, Jing L, Guo T, Cui H, Zhou J, Fu H, J. Phys. Chem. C., 113, 1006 (2009)
  31. Braconnier B, Paez CA, Lambert S, Alie C, Henrist C, Poelman D, Pirard JP, Cloots R, Heinrichs B, Micropor. Mesopor. Mater., 122, 247 (2009)
  32. Chen QF, Jiang D, Shi WM, Wu D, Xu Y, Appl. Surf. Sci., 255(18), 7918 (2009)
  33. Jing LQ, Fu HG, Wang BQ, Xin BF, Li SD, Sun JZ, Appl. Catal. B: Environ., 62(3-4), 282 (2006)
  34. Martyanov IN, Uma S, Rodrigues S, Klabunde KJ, Langmuir, 21(6), 2273 (2005)
  35. Nur H, Mater. Sci. Eng. B., 133, 49 (2006)
  36. Ren J, Li Z, Liu SS, Xing YL, Xie KC, Catal. Lett., 124(3-4), 185 (2008)
  37. Kim YK, Kim EY, Whang CM, Kim YH, Lee WI, J. Sol.Gel Sci. Technol., 33, 87 (2005)
  38. Lee IJ, Jung TS, Kim JG, Ro SH, Kim CS, Lee YJ, Kim YM, Lee JH, Kang MS, J. Ind. Eng. Chem., 14(6), 869 (2008)
  39. Mguig B, Calatayud M, Minot C, J. Mol. Struct. Theochem., 709, 73 (2004)
  40. Bollinger MA, Vannice MA, Appl. Catal. B: Environ., 8(4), 417 (1996)
  41. Iwamoto M, Yoda Y, Yamazoe N, Seiyama T, J. Phys. Chem., 82, 2564 (1978)
  42. Chon H, Pajares J, J. Catal., 14, 257 (1969)
  43. Li R, Ma JT, Xu JL, Zhou X, Su ZX, React. Kinet. Catal. Lett., 70(2), 363 (2000)
  44. Luo L, Shao G, Duan Z, Turk. J. Chem., 29, 597 (2005)
  45. Qu Z, Cheng M, Shi C, Bao X, J. Nat. Gas Chem., 14, 4 (2005)
  46. Bernal S, Calvino JJ, Cauqui MA, Gatica JM, Larese C, Omil JAP, Pintado JM, Catal. Today, 50(2), 175 (1999)
  47. Rui L, Inmaculada RR, Belen BB, Antonio GR, Sun G, Xin Q, Chin. J. Catal., 27, 109 (2006)
  48. Qu Z, Cheng M, Dong X, Bao X, Catal. Today., 93, 247 (2004)