The corrosion stability of vinyltriethoxysilane/epoxy coating protective system on aluminium is strongly related to the strength of bonds forming at the metal/organic coating interface. This article is a study of adhesion, composition, electrochemical and transport properties of epoxy coatings electrodeposited on bare aluminium and aluminium pretreated by vinyltriethoxysilane (VTES) during exposure to 3% NaCl. The VTES film was deposited on aluminium surface from 2% vinyltriethoxysilane solution during 30 s. From the values of adhesion strength (pull-off test), time dependence of pore resistance and coating capacitance of epoxy coating (impedance measurements) and diffusion coefficient of water through epoxy coating (gravimetric liquid sorption measurements), the influence of VTES sublayer on the corrosion stability of the electrodeposited epoxy coating was shown. The work discusses the role of the VTES pretreatment in the enhanced adhesion and corrosion stability of epoxy cataphoretic coating. The electrochemical results showed that the aluminium pretreatment by VTES film improved barrier properties of epoxy coating (greater pore resistance and lower coating capacitance). The lower value of diffusion coefficient of water through epoxy coating indicates the lower porosity, while the smaller adhesion reduction points to better adhesion of epoxy coating on aluminium pretreated by VTES film. The composition of the deposited coatings investigated by XPS enabled the clarification of the bonding mechanism. (C) 2009 Elsevier B. V. All rights reserved.