A simple method to prepare large-scale graphene sponges and free-standing graphene films using a speed vacuum concentrator is presented. During the centrifugal evaporation process, the graphene oxide (GO) sheets in the aqueous suspension are assembled to generate network-linked GO sponges or a series of multilayer GO films, depending on the temperature of a centrifugal vacuum chamber. While sponge-like bulk GO materials (GO sponges) are produced at 40 degrees C, uniform free-standing GO films of size up to 9 cm(2) are generated at 80 degrees C. The thickness of GO films can be controlled from 200 nm to 1 mu m based on the concentration of the GO colloidal suspension and evaporation temperature. The synthesized GO films exhibit excellent transparency, typical fluorescent emission signal, and high flexibility with a smooth surface and condensed density. Reduced GO sponges and films with less than 5 wt% oxygen are produced through a thermal annealing process at 800 degrees C with H-2/Ar flow. The structural flexibility of the reduced GO sponges, which have a highly porous, interconnected, 3D network, as well as excellent electrochemical properties of the reduced GO film with respect to electrode kinetics for the [Fe(CN)(6)](3-)/(4-) redox system, are demonstrated.