The miscibility and the thermal behaviour of chitosan acetate (ChA) with poly(vinyl alcohol) (PVA) have been investigated by differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and dynamic mechanical analysis (DMA). Chitosan is blended with poly(vinyl alcohol) in acetic acid solution and this solution is cast to prepare the blend film. From thermal curves the thermal transitions: T-g, T-m and characteristic temperatures of decomposition: T-di, T-max have been determined and compared. The influence of the degree of PVA hydrolysis on the thermal properties of blend systems has been discussed. Based upon the observation on the DSC analysis, the melting point of PVA is decreased when the amount of ChA in the blend film is increased. Though some broadening of the transition curves could be noticed (DSC, TGA and DMA), the obtained results suggest that in the solid ChA/PVA blends the components are poorly miscible. Only PVA sample with relatively low DH = 88% and hence low degree of crystallinity shows partial miscibility with ChA of relatively low molecular weight. (C) 2009 Elsevier B.V. All rights reserved.