New electroluminescent polymers with various phenyl groups, poly[2-dimethyl(octyl)silyl-5-(4-(dimethy](octyl)silyl)phenyl)-1,4-pheny lenevinylene] (P1), poly[2,5-bis(4-(dimethyl(octyl)silyl)phenyl)-1,4-phenylenevinylene] (P2), poly[2,5-bis(9,9-dihexylfluorenyl)-1,4-phenylenevinylene] (M), and poly [2,5-bis(4-(4-(2-etylhexyloxy)phenyl)phenyl)-1,4-phenylenevinylene] (P4), have been synthesized by the Gilch polymerization. The maximum absorption peaks of P1-P4 appeared at 388-423 nm in THF solution, and are red-shifted to 404-425 nm in solid thin film. The photoluminescence (PL) emission spectra of P1-P4 show a maximum peak at 482-503 nm in THF solution and at 521-549 nm as the solid film state. The emission spectra in the solid film state are more red-shifted over 40 nm, and the full width at half maximum (fwhm) was 30 nm greater than the solution conditions. The polymer light-emitting diodes (PLEDs) with the configuration of ITO/PEDOT/polymer/Al emitted light with maximum peaks at around 517-546 nm. The various phenyl substituents, with intermolecular interactions in the solid film state, can introduce the color tuning and device performance enhancement of the conjugated polymer as an emissive layer in PLED. Crown Copyright (C) 2008 Published by Elsevier Ltd. All rights reserved.