A facile and wet-chemical approach was employed to control synthesis of self-organizing, hyperbranched nanoporous Au microsheet with high quality in bulk quantity. This method produced nanoporous Au microsheets with a thickness of 7-15 nm. The microsheets were composed of irregularly interconnected planar Au nanoplates with interstices, i.e. nanopores of 10-50 nm. And the nanoporous Au microsheets were enveloped in 10-30 nm thick polyaniline (PANI) sheaths. The morphology of the nanostructured Au composites could also be easily tuned by changing the concentration of aniline and chlorauric acid. The dendritic and epitaxial growth of nanoporous Au microsheet was believed as the diffusion-limited process confined in the lamellar emulsion phase through self-assembly of aniline and dodecylsulfate. The solution reaction proceeded at a mild condition (room temperature and aqueous solutions), and less toxic reagents were employed instead of extreme toxic and corrosive chemicals. (C) 2009 Elsevier B.V. All rights reserved.