The influence of the length of a self-assembled monolayer (SAM) linker oil the electrochemical performance of electrode-linker-gold nanoparticle molecular constructs is investigated. Electrodes were first modified with amino-1-alkanethiols of four different lengths (C = 2,6,8, and 11). The SAM showed progressively greater blocking ability to ruthenium hexamine as the length of the alkyl chain increased to the point where no significant Faradaic peak was observed for the amino-1-undecanethiol SAM. Upon the attachment of gold nanoparticles, distinct Faradaic electrochemistry of the ruthenium hexamine was observed for all Four length SAMs with the electrochemistry being similar to that observed on it bare electrode. The charge transfer resistance to this Faradaic process was observed to be insensitive to the length of the intervening SAM, indicating it is electron transfer between the redox species and the nanoparticles, rather than tunneling across the SAM, which is the rate-limiting step. Some comments on the mechanism of charge transfer are provided. When forming multilayers of the linker-nanoparticle constructs, fabricated ill a stepwise manner, whenever the distal species was the SAM the Faradaic process wits blocked and whenever it was the nanoparticle a distinct Faradaic process was observed. With up to five layers of linker-nanoparticles, there was little increase in charge transfer resistance and again the charge transfer resistance was insensitive to the length of the linker.