In this report, we are presenting studies of the effect of MxOy nanopowders on the thermal, mechanical and electrical properties of [Nafion/(MxOy)(n)] membranes with M = Ti, Zr, Hf, Ta and W and n = 5 wt%. Five homogeneous membranes with thicknesses ranging from 170 to 350 mu m were Studied. The thermal transitions characterizing [Nafion/(MxOy)(n)] materials were investigated by modulated differential scanning calorimetry (MDSC). The mechanical parameters and relaxation processes were studied on temperature by dynamical mechanical analyses (DMA). Broadband dielectric spectroscopy (BDS) was used to study the conductivity mechanism and dielectric relaxation events in bulk materials. DMA investigations showed two distinct relaxation events. The first relaxation phenomenon, detected at about 19 degrees C, was attributed to the mechanical beta-relaxation mode of Nafion. The second event, revealed in the temperature range 100-135 degrees C, was assigned to the mechanical alpha-relaxation mode of Nafion. The electric response of membranes was studied by BDS measurements in the frequency and temperature range respectively of 40 Hz-10 MHz and 5-135 degrees C. Real and imaginary components of permittivity (epsilon*(omega) = epsilon' (omega) - i epsilon ''(omega)) and conductivity spectra (sigma*(omega) = sigma'(omega) + i sigma ''(omega)) were analyzed. Conductivity spectra allowed us to accurately determine the sigma(dc) of membranes at 100% RH as a function of T. Two relaxation peaks were detected in the epsilon*(omega) profiles. The low frequency relaxation event was attributed to the alpha-relaxation mode of fluorocarbon chains of Nafion. The high frequency relaxation peak corresponds to the beta-relaxation of acid side groups. The results allowed us to conclude that MxOy influences: (a) the relaxations of both the hydrophobic and the hydrophilic domains of Nafion polymer host; (b) the thermal stability range of conductivity (SRC) and the ad, of membranes. In conclusion, nanofillers affect the macromolecular dynamics of Nafion-based polymer host owing to the formation of dynamic cross-links, R-SO3H center dot center dot center dot MxOy center dot center dot center dot HSO3-R. in hydrophilic polar cages. The membranes doped with HfO2 and WO3 oxoclusters present a stability range of conductivity of 5 C <= T <= 135 degrees C and give rise to ad, values of respectively 2.8 x 10(-2) and 2.5 x 10(-2) S cm(-1) at 135 degrees C and 100% RH. These latter conductivity values make the nanocomposite membranes based on HfO2 and WO3 oxodusters; very promising materials for the application in polymer electrolyte fuel cells (PEMFCs) and direct methanol fuel cells (DMFCs). (c) 2008 Elsevier B.V. All rights reserved.