The thermal properties and phase morphology of poly(L-lactide) (PLLA)based blends have been studied. Two poly(ethylene glycol)s (PEGS) with molecular weight (MW) of about 1,500 (1.5k) g/mol and 2,000,000 (2M) g/mol, respectively, were used as counterparts. The blends were annealed at a preselected temperature of 200 degrees C for either 2 min or 30 min before the characterizations. Both PEGS were determined to enhance the crystallizability of PLLA. After a 2-min process of annealing, the PEG(1.5k)'s crystallization efficiency on PLLA has been noted to increase with the increase of its content. Conversely, PEG(2M)'s crystallization efficiency declined with the increase of its content. Extending the annealing time has evidently changed the PEGS' crystallization effect on PLLA. Moreover, the PEG(1.5k) has, to a greater extent, brought about the depression of PLLA's melting temperature by increasing its content, and this depression increased with the annealing time. The blends exhibited lower thermal stability than those of the parent components, particularly for the PEG(1.5k)-included system with a higher PEG content. Regardless of the annealing time, the PEG(1.5k)-included blends have shown homogeneous melt morphology under light microscope, whereas the PEG(2M)-included blends have displayed phase-separated melt morphology. In addition to the composition, PEG's MW and annealing time influence the crystalline morphology of the blends. The ringed PLLA spherulites have appeared mostly in the 2-min annealed PEG(1.5k)-included blends. (C) 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 1497-1510, 2009