Grape stalk is an organic waste produced in great amounts in the industrialization processes of grape. This work presents the results of studies carried out to use this waste as raw material to prepare activated carbon through the physical and chemical route. The physicochemical characterization of this material suggests the presence of unusually high levels of ashes. Metal content was determined and high levels of potassium, sodium, iron, calcium and magnesium in carbonized and raw grape stalk were exhibited. This characteristic made difficult physical activation at high temperatures. A leaching step was included before the activation with steam, and adsorbents with surface areas between 700 and 900 m(2)/g were obtained. Physical activation was also performed at lower temperatures using carbonized grape stalk without leaching, leading to the development of some grade of porosity, with an area of 472 m(2)/g. These results would indicate the catalytic effect of the minerals present in this raw material. Chemical activation using phosphoric acid as activating agent seemed to be a very efficient method as final products with BET areas between 1000 and 1500 m(2)/g were obtained. (C) 2009 Elsevier B.V. All rights reserved.