a-Plane GaN and AlGaN were grown on r-plane sapphire by low-pressure metal-organic vapor epitaxy (LP-MOVPE), and the effects of reactor pressure (from 40 to 500 Torr) and growth temperature (from 1020 to 1100 degrees C) on the crystalline quality and surface morphology of a-plane GaN were studied. The a-plane GaN grown under 40 Torr had a smooth-surface morphology but a poor crystalline quality; however, the a-plane GaN grown under 500 Torr had higher crystalline quality and optical properties, whose full-width at half-maximum of the X-ray rocking curve (XRC-FWHM) and intensity of yellow luminescence (YL) were smaller. Furthermore, the optical properties of a-plane GaN were investigated by photoluminescence (PL) in detail. We also studied the emission properties of a-plane Al0.35Ga0.65N grown at room temperature. (C) 2009 Published by Elsevier B.V.