With initial aging at low temperature for enough time, silicas with large mesoporosity were synthesized using triblock copolymer as template agent under weak acidities. SBA-15 with periodic mesostructure and short mesochannels could be synthesized at pH 2.5-3.0 within weak acidity range, and the surface areas, pore diameters and pore volumes reached up to ca. 1000 m(2)/g, 8.8 nm and 2.0 cm(3)/g, respectively, which were significantly higher than those of the conventional SBA-15 synthesized under strong acidities. Mesoporous silica with wormhole structure and abundant textural porosity was formed at pH similar to 3.5. The increased hydrophobic volume of the copolymer micelles at elevated pH values was responsible for the enlargement of mesoporosity in the products. The materials synthesized under weak acidities showed lower hexagonal ordering in comparison to the general SBA-15 synthesized under strong acidities because the decreased hydronium ion concentration induced relatively weaker assembly forces during the synthesis. Nonetheless, the short mesochannels and large pore diameter in the products might be beneficial to some applications in which fast diffusion of molecules is required. (C) 2009 Elsevier Inc. All rights reserved.