A mesoporous Ni-Al2O3 composite catalyst (Ni-A-NS) was prepared by a single-step non-ionic surfactant-templating method for use in hydrogen production by steam reforming of liquefied natural gas (LNG). For comparison, a nickel catalyst supported on mesoporous alumina (Ni/A-NS) was also prepared by an impregnation method. The effect of physicochemical properties on the performance of Ni-A-NS catalyst in the steam reforming of LNG was investigated. Ni-A-NS catalyst retained superior textural properties compared to Ni/A-NS catalyst. Nickel oxide species were highly dispersed on the surface of both Ni/A-NS and Ni-A-NS catalysts through the formation of surface nickel aluminate phase. Although both Ni/A-NS and Ni-A-NS catalysts exhibited a stable catalytic performance, Ni-A-NS catalyst showed a better catalytic performance than Ni/A-NS catalyst in the steam reforming of LNG. High nickel surface area and high nickel dispersion of Ni-A-NS catalyst played an important role in enhancing the dehydrogenation reaction of hydrocarbon species and the gasification reaction of adsorbed carbon species in the steam reforming of LNG. High reducibility of Ni-A-NS catalyst was also responsible for its high catalytic performance.