Three functional coatings (namely Al-C, Si-P-Al and P-F-Al coating) were fabricated by microarc oxidation method on Ti6Al4V alloy in different aqueous solutions. The microstructure, phase and chemical composition of coatings were investigated using scanning electron microscope, X-ray diffraction and energy dispersive spectroscopy. The interface adhesion failure mode of the coating is revealed by shear, tensile and thermal shock methods. The coatings exhibit high adhesion strength by the quantitative shearing test, registering as 110, 70, and 40 MPa for Al-C, Si-P-Al and P-F-Al coating, respectively. The tensile test of the coated samples shows that microarc oxidation treatment does not significantly deteriorate mechanical properties of substrate titanium alloy. The observations of the coating failure after subjected to the identical tensile elongation of 3.0% are well in agreement with those results of the shear test. The thermal cycle test indicates that all the coatings have good anti-thermal shocking properties. (C) 2009 Elsevier B.V. All rights reserved.