녹색과 청색 형광체 나노 분말의 합성 및 특성 평가
Formation and Characterization of Green and Blue Phosphor Nano Powders
E-mail:
초록
녹색과 청색의 나노 형광체 합성에 있어서 입자 형상 및 입자 크기의 변화를 알아보기 위해 액상법으로 진행하였으며, 이를 바탕으로 최종적으로 녹색 형광체의 경우 약 80 nm를, 그리고 청색 형광체의 경우 약 60 nm급의 나노 형광체 분말 합성이 가능하였다. 합성된 두 가지의 Zn2SiO4 : Mn 녹색 형광체와 BAM : Eu의 청색 나노 형광체 분말의 특성 평가를 비교하였으며, 그 결과 PL 특성면에서 녹색 형광체인 Zn2SiO4 : Mn이 BAM : Eu의 청색 형광체 대비 높은 형광성을 보여주었다.
Nano-sized green and blue phosphor powders were synthesized by liquid phase method to confirm the size and morphology. By using that process, the particle sizes of green and blue phosphor particles were 80 nm and 60 nm, respectively. The characteristic comparison of Zn2SiO4 : Mn and BAM : Eu was carried out and as a result, Zn2SiO4 : Mn powders showed an higher PL performance compared to BAM : Eu.
  1. Tachibani H, Mastsuda A, Haruk S, Kosugi N, Wani K, Weber LF, Proceedings of the 10th International Display Workshops [IDW’00] 651, Kobe, Japan, Nov. 29-Dec. 1 (2000)
  2. Tamatani M, J. Lumin., 100, 317 (2002)
  3. Yoon SJ, Jung YK, Seo JW, Lee BH, Kim YH, Kang BK, Displays, 23, 183 (2002)
  4. Hong GY, Jeoung BW, Jeon BS, Yoo JS, Ha CH, Whang KW, J. Electrochem. Soc., 151(10), H205 (2004)
  5. Jeoung BW, Hong GY, Han BY, Yoo JS, Jpn. J. Appl. Phys., Part 1, 43, 7997 (2004)
  6. Han BY, Yoo JS, Proceedings of the 5th Interna-tional meeting on information display [IMID’05], P-106, 1262, Daegu (2005)
  7. Han BY, Yoo JS, Kim YK, Heo EG, Choi CK, Kim JK, Eletrochem. Solid St., 11, J89 (2008)
  8. Ronda CR, Smets BMJ, J. Electrochem. Soc., 136, 570 (1989)
  9. Oshio S, Kitamura K, Shigeta T, Horii S, Matsuoka T, Tanaka S, Kobayashi H, J. Electrochem. Soc., 146(1), 392 (1999)
  10. Ronda CR, J. Alloys Comp., 225, 534 (1995)
  11. Verstegen JMPJ, Radielovic D, Vrenken LE, J. Electrochem. Soc., 121, 1627 (1974)
  12. Ravichandran D, Roy R, White WB, Erdei S, J. Mater. Res., 12, 819 (1997)
  13. Kutty TRN, Jagannathan R, Rao RP, Mat. Res. Bull., 25, 1355 (1990)
  14. Bae DS, Han KS, Cho SB, Choi SH, J. Kor. Association of Crystal Growth, 7, 167 (1997)
  15. Cho SB, Venigalla S, Adair JH, J. Am. Ceram. Soc., 79, 88 (1996)