The flame retardancy of polybutylene terephthalate (PBT) was studied focusing on the effect of various oxides. Thermo-gravimetric analysis, pyrolysis/gas chromatography/mass spectrometry, and elemental analysis (EA) were used to analyze the flame retardancy, which were observed through the UL-test and a cone calorimeter. Many oxides influenced the flame retardancy and some of them could suppress the flammability of PBT. In particular, the blended-PBTs with ZnO and V2O5 accelerated the degradation and the edges of oxygen consumption were shorter than neat-PBT although the flammability became poorer. The quantitative analysis of the scission products and the results of EA showed that hydrolysis, successive dehydration, and other various reactions changed the scission route to generate less flammable products. (C) 2008 Wiley Periodicals, Inc.