The authors present a new method for preparing thin films of SnO2 by atomic layer deposition (ALD) using alternating exposures to tetrakis(dimethylamino) tin and hydrogen peroxide. This method avoids problems of corrosion and agglomeration associated with the halogenated compound, SnCl4. Tin oxide films were successfully deposited on a variety of substrates using deposition temperatures of 50-300 degrees C at an average growth rate of 1.2 angstrom/cycle. They use in situ quartz crystal microbalance and quadrupole mass spectrometry measurements to explore the mechanism for SnO2 ALD. Scanning electron microscopy of SnO2 films deposited on Si(100) show that the SnO2 films are smooth, conformal, and nearly featureless, while atomic force microscopy yields a surface roughness of only 0.84 nm for a film with a thickness of 92 nm. X-ray diffraction reveals that the Sn02 films are amorphous. Films deposited on glass yielded a resistivity of similar to 0.3 Omega cm and an optical transmission of 94% for a film thickness of 140 nm. X-ray photoelectron spectroscopy measurements were consistent with residual dimethylamine ligands remaining in the film at deposition temperatures below 150 degrees C. This method allows, for the first time, low temperature (50 degrees C) growth of SnO2 films by ALD. Additionally, they show that this process is suitable for conformally coating high aspect ratio anodic alumina membranes. (C) 2008 American Vacuum Society.