Rice husk silica (RHS) in amorphous phase with 98% purity was prepared from a waste rice husk from rice milling by leaching with hydrochloric acid and calcination. The RHS was used effectively as a silica source for the synthesis of zeolite Y in sodium form (NaY). The zeolite in pure phase was obtained from a two-step synthetic route in which the starting gels were mixed, aged for 24 h at room temperature and crystallized for 24 h at 90 ℃. The diameter of single crystal particles from a scanning electron microscope was approximately 1.0 μm, whereas the average particle diameter from laser diffraction particle size analyzer was approximately 10 μm because of the agglomeration of small crystals. Longer crystallization time in this route resulted in a mixed phase containing NaY and zeolite P in sodium form (NaP). In addition, a one-step synthetic route (no aging) was studied and the product was also a mixed phase zeolite.