In this study, a self-constrained BaTiO3 material system, composed of a low-fire BaTiO3-based X7R (Delta C/C +/- 15% within -55 degrees to 125 degrees C) MLCC dielectric and a high-fire, BaTiO3-based X7R MLCC dielectrics eliminated sintering aid that are laminated on both sides of the BaTiO3-based X7R MLCC, has been developed. The temperature dependence of capacitance of the BaTiO3-based X7R MLCC is significantly improved to satisfy X8R requirements over the entire temperature range studied (Delta C/C +/- 15% within -55 degrees to 150 degrees C) using the self-constrained sintering. The curie temperature of BaTiO3-based X7R MLCC increases on increasing the thickness of the constraining layers. Compared with the specimen fired by free sintering, a substantial reduction in grain size, leading to a decrease in dielectric constant, was observed in the specimen fired by constrained sintering with the thickness of the constraining layer being 170 mu m. The increase in Curie temperature and decrease in grain size of the specimen fired by constrained sintering can be explained in terms of the presence of in-plane tensile stress. The in-plane tensile stress that introduces a friction force between the multilayer matrix and the nonshrinkage constraining layers to suppress the in-plane shrinkage and to inhibit the rate of grain growth was formed during constrained sintering.