Polyurethanes containing poly(2-trifluoroethoxymethyl-2-methyl)-co-(2-bromomethyl-2-methyl)-1,3-p ropylene oxide (co-polyoxetane) soft blocks, P[3FOx:BrOx-m:n], were prepared and used (0.5-2 wt %) to modify the surface properties of a conventional polyurethane. The substrate polyurethane was composed of an isophorone diisocyanate/butanediol hard block and a polytetramethylene oxide soft block [IPDI/BD(50%)-PTMO(2000)]. A combination of tapping mode atomic. force microscopy (TM-AFM), X-ray photoelectron spectroscopy (XPS), and dynamic contact angle (DCA) studies showed that the fluorous polyurethane surface modifiers confer surface properties similar to those of the parent at 0.5-1.0 wt %. The retention of initial wetting behavior in water was enhanced with higher ratios of 3FOx:BrOx that corresponds to increasing fluorous character. A semifluorinated chaperone is necessary to surface concentrate -CH2Br groups. Negligible Br was detected by XPS when the P[BrOx]-soft block polyurethane was used as a surface modifier (0.5%) and the wetting behavior was similar to that of the bulk polyurethane. Despite being hydrophobic (theta(adv) = 102 degrees) the P[BrOx]-soft block polyurethane is not a polymer surface modifier under the conditions described herein. The calculated solubility parameters for PTMO and P[BrOx], which are similar, support the notion of BrOx miscibility with the base polyurethane. The combination of miscibility of BrOx repeat units and lack of an end-group-like architecture minimizes BrOx surface concentration in the chosen bulk polyurethane.