A novel layered AgBr-based inorganic/organic nanocomposite was prepared by pulsed laser ablation (PLA) of Ag in aqueous media in the presence of cetyltrimethylammoniurn bromide (CTAB), and the formation mechanism of two-dimensional nanosheet was discussed. TEM observations indicate that the obtained AgBr-based inorganic/organic nanocomposite possesses a well-defined two-dimensional shape and that the size of the nanosheet can be changed with the surfactant concentration in the solution. X-ray diffraction (XRD) pattern was composed of a series of peaks that could be indexed to (001) reflections of a layered structure, and the basal spacing of 20.0 angstrom indicated that the surfactant was included between the AgBr interlayers in an interdigitated bilayer arrangement. In contrast, a layered inorganic/organic nanocomposite cannot be formed at a CTAB concentration lower than the critical micelle concentration (CMC). Based on our detailed investigation, we proposed the nanocomposite formation process, that is, that negatively charged inorganic AgBr was produced by a strong reaction between the ablated Ag species and the bromide ions, which are concurrently assembling with cationic surfactant molecules controlled by the charge-matching mechanism.