While there are numerous studies examining the performance of lithium titanate spinel (LTS) as a lithium-ion battery, little is known about the surface chemistry of this material. In this paper, diffuse reflectance infrared Fourier transform (DRIFT) spectroscopy spectroscopy was used to study the type of surface groups present on LTS as a function of temperature. The surface was found to contain isolated and hydrogen-bonded TiOH groups and the dehydroxylation behavior with thermal treatment was similar to that of TiO2. In addition, hexamethyldisilazane (HMDZ) and pyridine were used to probe the reactivity of surface hydroxyl groups and the presence of Lewis acid sites, respectively. The reaction of HMDZ occurred with both LiOH and TiOH groups to form Li-O-Si and Ti-O-Si. In addition, the reaction of gaseous CO2 with the Li+ ions resulted in the formation of surface carbonate ions. The carbonate ions are removed by heating at 400 degrees C in air. (C) 2007 Elsevier B.V. All rights reserved.