We report the synthesis of poly N-(2-hydroxypropyl)methacrylamide ordered arrays of fluid filled channels. The polymerization and crosslinking reactions are carried out under the influence of a constant electric field (60 V/cm). A charged comonomer, immobiline (pK 3.6), and porogen, polyethylene glycol (PEG) are added to the pregel solutions. Scanning electron microscopy reveals that the channels have a typical diameter of 2-25 mu m and are oriented parallel to the electric field employed during synthesis. The self-organization of channels occurs around an optimal PEG concentration of 8.6 wt/vol %, whereas significantly higher or lower concentrations yield random, isotropic pore structures. Moreover, tensile strength measurements show that the mechanical stability increases with decreasing concentration of PEG. Rheology experiments reveal that the swelling degree of these superabsorbant hydrogels increases with increasing PEG. Possible applications of these microstructured. hydrogels as bidirectional scaffolds for regenerating neurons in the injured spinal cord are discussed. (c) 2007 Wiley Periodicals, Inc.