In this work, a fabrication process of piezoelectric PZT [Pb(Zr0.52Ti0.48)O-3] thick films up to 60 mu m deposited on silicon and aluminum substrates is reported. Crystalline spherical modified PZT powder about 300 nm in diameter was used as filler. PZT polymeric precursor produced by Chemat Inc. was used as the matrix material. Spinning films were annealed at 700 degrees C for one hour in the furnace in air. The thickness of the thick films was measured using a scanning electron microscope (SEM). Compared with previous piezoelectric PZT composite films, the modified piezoelectric thick films exhibit better dielectric properties. The dielectric constant is over 780 and dielectric loss is 0.04 at 1 KHz. Using a PiezoCAD model, the high frequency transducer was designed and fabricated. It showed a bandwidth of 75% at 40 MHz.