crystal structural characteristics of the fluoro carbon poly(tetra fluoro ethylene) (PTFE) have been studied by X-ray diffraction methods. The initial hexagonal arrangement of the PTFE chains in a 157 helical conformation is left unaffected by the exposures to temperatures (T), up to and beyond its melting point, T,. The unit cell registers a residual anisotropic volume expansion. The anisotropy arises from the enhanced enlargement of the basal plane dimension a compared with the axial dimension c. Conformational changes contributing to the observed increase in the chain length have been examined. Enhancement of residual crystallinity of samples aged at T's < T-m suggests that the selective thermal aging could be used as an effective tool to improve the initial crystallinity of commercially available PTFE. The activation energy for 50% enhancement in initial crystallinity has been estimated as 53.9 kJ mol(-1). Aging at 400 degrees C, a temperature above T-m, is accompanied by markedly different features viz., deterioration in crystallinity and other structural characteristics. The overall behavior of thermally aged PTFE bears a marked similarity to many polyamides.