The vinylic polymerization of norbornene and its copolymerization with norbornene carboxylic acid methyl esters were investigated. Norbornene was polymerized by us using di-mu-chloro-bis-(6-methoxy-bicyclo[2.2..1]hept-2-ene-endo-5 sigma,2 pi)-palladium(II) as catalyst. The polymerization time can be decreased by a factor of 100000 by activation of the catalyst with methylaluminoxane (MAO). With this palladium catalyst activated by MAO, 140 t of norbornene can be polymerized per mol palladium per h. This catalyst system was much more active than [Pd(CH3CN)(4)](BF4)(2) (I). The polymerization of norbornene by (6-methoxybicyclo[2.2..1]hept-2-ene-endo-5 sigma,2 pi)-palladium(II) tetrafluoroborate was also possible but it was not as fast as the polymerization by Pd catalysts activated with MAO. We were also able to obtain copolymers of norbornene and 5-norbornene-2-carboxylic acid methyl ester (exo/endo = 1/4 or 2/3) containing between 15 and 20 mol-% ester units. The copolymerization of norbornene and 2-methyl-5-norbornene-2-carboxylic acid methyl ester (exo/endo = 7/3) was faster than the copolymerization mentioned before. In contrast the homopolymerization of 2-methyl-5-norbornene-2-carboxylic acid methyl ester was 10 times slower than that of 5-norbornene-2-carboxylic acid methyl ester (exo/endo = 1/4).