A novel biodegradable polyester having pendant amine functional groups was snythesized from N-(benzyloxycarbonyl)-L-aspartic anhydride (2) and 1,4-cyclohexanedimethanol (3) by polycondensation reaction using p-toluenesulfonic acid as a catalyst. The synthesized polymer 4 shows the characteristic eater carbonyl absorption peak at 1732 cm(-1) in the LR spectrum, and the NMR spectra were consistent with the IR data. Also, the elemental analysis showed that the experimental and calculated values were very close to each other. The weight-average molecular weight of the polymers ranged from 1140 to 5050 and increased with increasing reaction time. This new polymer would have the potential of a drug delivery biomaterial.