Pressure, volume, temperature (PVT) measurements reveal that during the intramolecular cyclization reaction of poly(acrylonitrile) (PAN) and poly(styrene-co-acrylonitrile) (SAN) the volume decreases. This volume contraction becomes smaller with increasing styrene content in the random copolymers and should be related to the simultaneous decrease of longer acrylonitrile home-sequences. The onset temperature of the cyclization reaction is raised with higher styrene contents in the random copolymers. Thus, it can be excluded that the cyclization reaction has a major influence on the discoloration process of SAN samples having relatively small acrylonitrile contents (less than 50 mol-%) during thermal annealing below 300 degrees C.