A new preparation process for carbon nanotubes (CNTs) cold cathode was studied through the replacement of traditional organic or inorganic binder with Ag nano-particles. This method has the advantages of low preparation temperature and fine electrical contact between CNTs paste and substrate. A mixture paste of CNTs, Ag nano-particles and other organic solvents was spreaded on Si substrate. By melting and connecting of Ag nano-particles after sintered 30 min at 250 degrees C, a flat CNTs films with good field emission properties was obtained. The measurements reveal that the turn on electric field and the threshold electric field of as-prepared CNTs cathode are 2.1 and 3.9 V/mu m respectively and the field emission current density is up to 41 mA/cm(2) at an applied electric field of 4.7 V/mu m. (c) 2006 Elsevier B.V. All rights reserved.