Nanoporous silica materials with uniform pore size and ordered structure have drawn growing interest of researchers since 1990s. A large-pore nanoporous material, SBA-15, was functionalized with organosilanes by co-condensation method in the presence of nonionic triblock copolymer P123 as a template under acidic conditions. The functionalization was demonstrated by using five organosilanes, namely 3-aminopropyltriethoxysilane (APTES), 3-mercaptopropyltrimethoxysilane (MPTMS), phenyltrimethoxysilane (PTMS), vinyltriethoxysilane (VTES), and 4-(triethoxysilyl)butyronitrile (TSBN), which modified the surface properties of the silica materials, enabling the materials to be a promising support for immobilization of biological molecules. The functionalized SBA-15 materials exhibited long-range ordering of two-dimensional hexagonal pore arrays of size ranging from 66 to 90 Angstrom as demonstrated by small-angle X-ray scattering (SAXS), transmission electron microscopy (TEM), and physical adsorption techniques. A variety of organosilane density in the range of 0.5-2.6 mmol/g was achieved as revealed by elemental analysis and solid-state nuclear magnetic resonance (NMR) techniques. The functionalized materials displayed improved properties for immobilization of penicillin acylase (PA) in comparison with pure-silica SBA-15. Such improvement is believed to be due to the enhanced surface hydrophobicity and electrostatic interactions of the functional groups with the enzyme. (C) 2004 Elsevier B.V. All rights reserved.