Journal of Crystal Growth, Vol.250, No.3-4, 450-457, 2003
Characteristic crystal growth from amorphous WO3 film by vacuum heating
Selective growth of WO2, W and WO3-x crystals from amorphous WO3 film by vacuum heating at 400-900degreesC was clarified. The grown WO3-x crystals were incommensurate structure based on crystallographic share structure. The growth process of WO2 crystal in the amorphous film was directly observed at high temperature in the electron microscope. The growth front of the WO2 crystal consumes WO3 microcrystallites with various orientations. The growth speed of the WO2 depended on WO3 microcrystallites orientation. The origin of the wavy growth front of WO2 was due to an orientation dependence of the WO3 microcrystallites. (C) 2003 Elsevier Science B.V. All rights reserved.