Heavily doped barium titanate (BaTiO3) powders, one with a donor-rich and the other with an acceptor-rich composition, were prepared. After sintering, the donor-rich specimen exhibited a fine-grained microstructure but significant grain growth occurred in the acceptor-rich specimen. A stable dielectric behavior was observed only in the donor-rich fine-grained specimen over the temperature range studied. However, in both specimens, an undoped core region several hundred nanometers in size was detected. The core-shell structure appeared to be maintained in BaTiO3 under the conventional sintering conditions.