The temperature dependence of tensile fracture behavior and tensile strength of a two-dimensional woven BN-coated Hi-Nicalon (TM) Sic fiber-reinforced Sic matrix composite fabricated by polymer infiltration pyrolysis (PIP) were studied. A tensile test of the composite was conducted in air at temperatures of 298 (room temperature), 1200, 1400, and 1600 K. The composite showed a nonlinear behavior for all the test temperatures; however, a large decrease in tensile strength was observed above 1200 K. Young's modulus was estimated from the initial linear regime of the tensile stress-strain curves at room and elevated temperatures, and a decrease in Young's modulus became significant above 1200 K. The multiple transverse cracking that occurred was independent of temperature, and the transverse crack density was measured from fractographic observations of the tested specimens at room and elevated temperatures. The temperature dependence of the effective interfacial shear stress was estimated from the measurements of the transverse crack density. The temperature dependence of in situ fiber strength properties was determined from fracture mirror size on the fracture surfaces of fibers. The decrease in the tensile strength of the composite up to 1400 K was attributed to the degradation in the strength properties of in situ fibers, and to the damage behavior exception of the fiber properties for 1600 K.