Journal of Industrial and Engineering Chemistry, Vol.13, No.2, 319-324, March, 2007
Preparation of Platinum and Palladium Nanotubes Using MPTMS-Functionalized Silica Spheroids as Templates
E-mail:
Platinum and palladium nanotubes were prepared by the adsorption of metal nanoparticles onto functionalized silica templates. The silanizing agent 3-mercaptopropyl trimethoxysilane was reacted with the surface of the silica templates to present thiol-terminal groups. Dissolution of the silica template using 10 M HF solution enabled the formation of self-organized metallic platinum and palladium nanotubes. When the temperature of the metal reduction process was increased from 4 to 80 ℃, this method was more effective than the metal reduction conducted at room temperature. The platinum and palladium nanotubes were characterized by field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS).
  1. Iijima S, Nature, 56, 354 (1991)
  2. Bo XZ, Lee CY, Strano MS, Goldfinger M, Nuckolls C, Blanchet GB, Appl. Phys. Lett., 86, 182102 (2005)
  3. Staii C, Johnson AT, Chen M, Gelperin A, Nano Lett., 5, 1774 (2005)
  4. Shim M, Javey A, Kam NWS, Dai HJ, J. Am. Ceram. Soc., 123, 11512 (2001)
  5. Bao J, Tie C, Xu Z, Zhou Q, Shen D, Ma Q, Adv. Mater., 13, 1631 (2001)
  6. Son SJ, Reichel J, He B, Schuchman M, Lee SB, J. Am. Chem. Soc., 127(20), 7316 (2005)
  7. Fan R, Karnik R, Yue M, Li D, Majumdar A, Yang P, Nano Lett., 5, 1633 (2005)
  8. Lahav M, Sehayek T, Vaskevich A, Rubinstein I, Angew. Chem.-Int. Edit., 42, 5576 (2003)
  9. Sun Y, Mayers BT, Xia Y, Nano Lett., 2, 481 (2002)
  10. Luo Y, Lee SK, Hofmeister H, Steinhart M, Gsele U, Nano Lett., 4, 143 (2004)
  11. Steinhart M, Jia Z, Schaper AK, Wehrspohn PB, Gsele U, Wendorff JH, Adv. Mater., 15, 706 (2003)
  12. Kijima T, Yoshimaru T, Uota M, Ikeda T, Fujikawa D, Mouri S, Uoyama S, Angew. Chem.-Int. Edit., 43, 228 (2004)
  13. Lahav M, Sehayek T, Vaskevich A, Rubinstein I, Angew. Chem.-Int. Edit., 42, 5576 (2003)
  14. Mayers B, Jiang XC, Sunderland D, Cattle B, Xia YN, J. Am. Chem. Soc., 125(44), 13364 (2003)
  15. Stober W, Fink A, Bohn E, J. Colloid Interface Sci., 26, 62 (1968)
  16. Lindberg R, Sjblem J, Sundholm G, Colloids Surf. A: Physicochem. Eng. Asp., 99, 79 (1995)
  17. Lee YG, Oh C, Yoo SG, Koo SM, Oh SG, Microporous Mesoporous Mater., 86, 134 (2005)
  18. Hwang YJ, Lee YH, Oh C, Jun YD, Oh SG, J. Ind. Eng. Chem., 12(3), 380 (2006)
  19. Moulder JF, Stickle WF, Sobol PE, Handbook of X-ray Photoelectron Spectroscopy, p.78, Perkin-Elmer (1993)
  20. Oh C, Lee YG, Park JH, Oh SG, Colloids Surf. A: Physicochem. Eng. Asp., 269, 112 (2005)
  21. Lee SK, Lee J, Joo J, Hyeon T, Ahn WS, Lee HI, Lee CH, Choi W, J. Ind. Eng. Chem., 9(1), 83 (2003)
  22. Park JH, Kim YG, Oh C, Shin SI, Kim YC, Oh SG, Kong SH, Mater. Res. Bull., 40, 271 (2005)
  23. Moulder JF, Stickle WF, Sobol PE, Handbook of X-ray Photoelectron Spectroscopy, p. 118, Perkin-Elmer (1993)