Electrospun polymeric narrofibres have several applications because of their high surface area to volume and high length to diameter ratios. This paper investigates the influence of plasma etching on these fibres and the etching mechanisms. For the characterization, SEM analysis was performed to determine the forms and shapes of the fibres and SEM photos were analysed by the technique of mathematical morphology, in order to determine the area on the sample occupied by the fibres and the frequency distribution of the nanofibre diameters. The results showed that the oxygen plasma etches the nanofibres much faster when ion bombardment is present. The form of the fibres is not altered by the etching, indicating the possibility of transport of oxygen atoms over the fibre surface. The most frequent diameter, somewhat surprisingly, is not significantly dependent on the etching process, and remains of the order of 80 nm, indicating that fibres with smaller diameters are etched at high rates. (c) 2005 Elsevier B.V. All rights reserved.